TPV SOLUTIONS

Contact TPE Sales Department

Enflex-V® is our brand name for dynamically vulcanized ethylene/propylene/diene (EPDM) and Polypropylene (PP) blends. Fully cured EPDM particles that are homogenously distributed in the thermoplastic polypropylene phase give these compounds unique rubber-like properties, with the advantage of thermoplastic processing techniques.

Enflex-V® range can be self-colored with the use of proper MB or provided as pre-colored compounds.

Key Properties

  • Hardness range from 45 Shore A to 60 Shore D
  • Service Temperature: -50°C – +125°C (dynamic) -50- + 135°C (Static/Peak)
  • Excellent ozone, UV and weather resistance due to saturated elastomeric phase
  • Chemical resistance to aggressive mediums
  • Very Low (Rubberlike) compression set and good elasticity (that does not change significantly over time) in a wide temperature range
GradesHardness Sh A / Sh D
ISO 868 (15 Sec)
Density gr / cm³
ISO 1183 1-A
Tensile Strength
Mpa ISO 37
Elongation at
Break,% ISO 37
Modulus %100
Mpa ISO 37
Tear Strength
Mpa ISO 34-1
Compression set at 22h 70C
ISO 815 typeB
ENFLEX VL120-60A60 A0,975,15302,11928
ENFLEX VL120-70A70 A0,976,75402,82536
ENFLEX VL120-80A80 A0,978,75503,93348
ENFLEX VL120-40D40 D0,94186008,98053
GradesHardness Sh A / Sh D
ISO 868 (15 Sec)
Density gr / cm³
ISO 1183 1-A
Tensile Strength
Mpa ISO 37
Elongation at
Break,% ISO 37
Modulus %100
Mpa ISO 37
Tear Strength
Mpa ISO 34-1
Compression set at 22h 70C
ISO 815 typeB
ENFLEX VU420-60A60 A0,975,55501,52732
ENFLEX VU420-70A70 A0,9775502,64138
ENFLEX VU420-80A80 A0,978,86303,96044
ENFLEX VU420-40D40 D0,97166708,210555
VU420-65A-T1-76565 A0,976,95502,23937

Application
DensityRavago Code
1,35VM-564-85A-F0-000
1,35VO-564-65A-F0-000
1,25VO-574-70A-F0-000
1,25VO-574-80A-F0-000 (UL listed)
1,25VO-584-40D-F0-000 (UL listed)
ENFLEXInjection/Extrusion1,25VO-584-60A-F0-000
1,25VO-584-90A-V0-000
1,04VL-545-35D-F0-000
1,04VL-545-60A-F0-000
1,04VL-545-70A-F0-000
1,04VL-545-80A-F0-000
1,04VL-545-90A-F0-000

Most TPV products on the market are moisture sensitive. We have recently developed a new proprietary cure system and manufacturing process to make non- hygroscopic TPV products.  Since these products are not hygroscopic, they do not need drying prior to thermoplastic processing.

They also exhibit improved color with low yellowness for the ability to color match a wide range of colors with very little variation or color drift. 

These new materials have good oil resistance and mechanical resilience properties that are superior to other TPV materials.

Key Properties

  • Hardness from 55 to 85 Shore A
  • Very high fluidity
  • Non-hygroscopic – no need to dry before processing
  • Easier coloring (less MB)
  • Faster cycle time & easier processing
GradesHardness Sh A / Sh D
ISO 868 (15 Sec)
Density gr / cm³
ISO 1183 1-A
Tensile Strength
Mpa ISO 37
Elongation at
Break,% ISO 37
Modulus %100
Mpa ISO 37
Tear Strength
Mpa ISO 34-1
Compression set at 22h 70C
ISO 815 typeB
EZPRENE VL320-60A60 A0,9655501,93037
EZPRENE VL320-70A70 A0,967,25702,84533
EZPRENE VL320-90A90 A0,96105705,87747
GradesQB36
Approval
Class
ColorHardness
Sh A
ISO 868 (15 sec)
Density
gr / cm³
ISO 1183 1-A
Tensile
Strength
Mpa
ISO 37
Elongation at
Break,%
ISO 37
Compression
set at 22 h
70C
ISO 815-1
EZPRENE VL321-65A-T4-000C4,5NATURAL650,97865035
EZPRENE VL321-65A-T4-766C4,5GREY650,97865035
EZPRENE VL321-65A-T4-900C4,5BLACK650,97865035
ENSOFT SD141-60A-T2-0005NATURAL601,08775035
GradesHardness Sh A / Sh D
ISO 868 (15 Sec)
Density gr / cm³
ISO 1183 1-A
Tensile Strength
Mpa ISO 37
Elongation at
Break,% ISO 37
Modulus %100
Mpa ISO 37
Tear Strength
Mpa ISO 34-1
Compression set at 22h 70C
ISO 815 typeB
EZPRENE VU320-60A60 A0,9776501,52737
EZPRENE VU320-70A70 A0,977,57002,33739
EZPRENE VU320-90A90 A0,97156504,540

Application
DensityRavago Code
0,9VX-201-55A-T2-000
0,9VX-201-60A-T2-000
EZPRENEHighflow Injection0,9VX-201-65A-T2-000
0,9VX-201-70A-T2-000
0,9VX-201-75A-T2-000

More Information

See More

SEBS COMPOUNDS
SBS COMPOUNDS
TPO COMPOUNDS

Based on saturated styrenic block copolymer SEBS (styrene-ethylene-butylene-styrene) and polyolefins mainly polypropylene (PP)

Unsaturated styrenic block copolymer, SBS (styrene-butadiene-styrene) based compounds

TPO compounds are resin blends of polypropylene (PP) and un-crosslinked EPDM rubber and polyethylene.